 Austenitic
|
|
Mechanical Composition (%) |
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
etc |
|
301 |
≤0.15 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
16.0~18.0 |
6.0~8.0 |
|
|
301L |
≤0.03 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
16.0~18.0 |
6.0~8.0 |
N≤0.20 |
|
304 |
≤0.08 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
18.0~20.0 |
8.0~10.5 |
|
|
304L |
≤0.03 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
18.0~20.0 |
9.0~13.0 |
|
|
304J1 |
≤0.08 |
≤ 1.70 |
≤ 3.00 |
≤ 0.045 |
≤ 0.030 |
15.0~18.0 |
6.0~9.0 |
Cu 1.00~3.00 |
|
305 |
≤0.12 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
17.0~19.0 |
10.5~13.0 |
|
|
316 |
≤0.08 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
16.0~18.0 |
10.0~14.0 |
Mo 2.0~3.0 |
|
316L |
≤0.03 |
≤ 1.00 |
≤ 2.00 |
≤ 0.045 |
≤ 0.030 |
16.0~18.0 |
12.0~15.0 |
Mo 2.0~3.0 |
|
321 |
≤ 0.08 |
≤ 1.00 |
≤2.00 |
≤ 0.045 |
≤ 0.030 |
17.0~19.0 |
9.0~13.0 |
Ti5xC% |
|
|
Ferritic
|
|
Mechanical Composition (%) |
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
etc |
|
409L |
≤ 0.03 |
≤ 1.00 |
≤ 1.00 |
≤ 0.040 |
≤ 0.03 |
10.5~11.7 |
6.0~8.0 |
Ti6xC% ~0.75 |
|
430 |
≤0.12 |
≤ 0.75 |
≤1.00 |
≤ 0.040 |
≤ 0.03 |
16.0~18.0 |
≤0.60 |
|
|
430J1L |
≤0.025 |
≤ 1.00 |
≤ 1.00 |
≤ 0.040 |
≤ 0.03 |
16.0~20.0 |
≤0.60 |
N 0.025  , Cu 0.30~0.80 Nb8x(C%+N%)~0.80 |
|
436L |
≤0.025 |
≤ 1.00 |
≤1.00 |
≤ 0.040 |
≤ 0.03 |
16.0~19.0 |
≤0.60 |
Mo 0.75~1.25 , , N 0.025 , Ti, Nb, Zr 8x(C%+N%)~0.80 |
|
444 |
≤0.025 |
≤ 1.00 |
≤ 1.00 |
≤ 0.040 |
≤ 0.03 |
17.0~20.0 |
≤0.60 |
Mo 1.75~0.50,
N 0.025 Ti, Nb, Zr 8x(C%+N%)~0.80 |
Martensitic
|
|
Mechanical Composition (%) |
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
etc |
|
410 |
≤ 0.15 |
≤ 1.00 |
≤ 1.00 |
≤ 0.04 |
≤ 0.03 |
11.5~13.5 |
≤0.60 |
|
|
420J1 |
0.16 ~0.25 |
≤ 1.00 |
≤ 1.00 |
≤ 0.04 |
≤ 0.03 |
12.0~14.0 |
≤0.60 |
|
|
420J2 |
0.26 ~0.40 |
≤ 1.00 |
≤ 1.00 |
≤ 0.04 |
≤ 0.03 |
12.0~14.0 |
≤0.60 |
| |
|